UV 减粘保护膜

2016/5/29 15:37:01      点击:
 

Feature


1.     初始超高的剥离强度,可以紧密的贴覆于平面、曲面被保护物表面,如果用于载带,则可确保其表面的微

The highly adhesion before the UV curing could high closely joint the glass or metal's surface, if the tape use for carrier tape, the tiny components will stable

小元器件不会发生相对移动,无论制程震动如何强烈,都不会使保护膜脱离

on the tape,no matter how strong vibration of the production

2.     UV减粘后其剥离强度可低于5gf/inch,极易从被保护物表面揭离

The lowest peel strength after UV curing can be achieved 5 gf / inch or less, easily peel from every substrate

3.     UV减粘后的剥离强度客户可通过调节其UV灯型、光照强度以及能量大小获取其制程所需最佳剥离强度

About the Peel strength after UV curing customers can get their optimum peel strength for production by adjusting the UV light type, light intensities and energy value


结构Construction


离型层

Release Layer

uv胶层

UV Layer

PET层

PET Layer


用途及特性Usage and characteristic


•电子微小器件载带,玻璃酸洗保护

Tiny electronic component’s carrier tape; Acid washed glass protection.

•玻璃、金属等的曲面保护

Glass, metal surface protection

•其他需要高粘紧密贴合保护,后期需要易撕离的制程保护

Others need high closely joint protection at beginning and easily to be peeled off after processing procedure.


产品型号Product Type

PUV100A

PUV100B

PUVC100A

PUVC100B

使用层厚度Using Layer Thickness ( JilTL)

116

116

116

116

PET厚度PET Thickness ( jim )

100

100

100

100

胶层厚度Adhesive Layer Thickness ( (-11T1)

16

16

16

16

离型月旲厚度Release Film Thickness (jllll)

50

50

50

50

剥离强度

Peel Strength (gf/inch)

过UV前

2500

2200

2500

2200

过UV后

<5

<20

<5

<20

A.    在生产之日起180天内使用,可获得最佳的使用性能


Use within180days from the date of production,to get the best performance

B.   请于23±5"C、65 %RH以下的环境下保存,置于阴凉处保存

Please at23 ± 5°C,65%RH under the following environmental preservation, placed in shady place

c.以上是代表值,不是保证值,未经确认不能作为交易的依据,基材厚度等可根据客户要求调整

Above are representative values, not guaranteed values, can't serve as the basis unconfirmed transactions Substrate thickness can be adjusted according to customer requirements